Influence of the cleaning method employed prior to the use of ionomeric materials in micro filtration of cavities at the cervical level
Keywords:
Vitreo ionomer cements, Dental Filtration, Aluminum Oxide.Abstract
Objective: To evaluate the influence of the cleaning of the cavity with aluminum oxide and pumice on the marginal microfiltration when using ionomeric materials (IV). Materials and Methods: In 40 human premolar teeth, cavities were prepared at the level of the cemetery amelo, the teeth were randomly divided into 4 groups (n: 10) received cleaning and restoration procedures according to the group, G1 cleaning with abrasive air and restoration with IV Ketac Molar Easy Mix (IVKM), G2 abrasive air and restoration with IV Gold Label 2 (IVGL), G3 pumice stone and IVKM, G4 pumice stone and IVGL. After the process of thermal aging, pigmentation with methylene blue and cutting in the lingual buccal direction, the fragments with the highest integrity were analyzed to the stereomicroscope by three evaluators who established the degree of micro filtration at the cervical and occlusal levels; the average obtained by surface per tooth was analyzed statistically. Results: The analysis performed revealed normality in the data, finding through the Tukey test that all groups are equal, with no difference in treatment and material used. Conclusions: Micro filtration was evident in all the groups independent of the cleaning treatment and the restoration material used, most notably at the level of the cervical wall.
Downloads
References
Barceló F, Sánchez J, Serrano C, Guerrero J. Estudio comparativo de ionómeros de vidrio y reforzados con metal. ADM. 1999; 6(5): 177-181.
Litonjua L, Andreana S, Bush P, Cohen R. Tooth wear: Attrition, Erosion, and Abrasion. Quintessence Int.l. 2003 Junio; 34(6):435-46.
Rees JS JP. The effect of interfacial failure around a class V composite retauration analysed by the finite element method. J Oral Rehabil. 2001 December; 27(2):111-116.
Hidalgo- Lostaunau R MRM. Ionomeros de vidrio convencionales como base en la técnica restauradora de sándwich cerrado: su optimización mediante la técnica de acondicionamiento ácido simultáneo y selectivo. Acta Odontol Venez. 2009; 47(4): 273-276.
Lahod V. Cementos a base de vidrio ionomero. Odontología Sanmarquina. 1999; 1(1): 1-3.
Calabria H. Lesiones no cariosas del cuello dentario: patología moderna, antigua controversia. Odontoestomatología. 2009 Mayo ; 11(12): 177.
Gil. M GG,LD. Terapéutica de las lesiones cervicales. Caracas : Fac. Odontología. UCV; 2013 Febrero.
Pereira I, Belkiss F, Silva J, Conceição R, Silami C, Mantovani F, et al. Influence of surface treatment on the performance of silorane-based composite resin in class I restorations: a randomized clinical trial. Clin Oral Invest. 2018 Febrero:1-8.
kumar U, Dharmani C, Singh S, Logani A, Shah N. Effect of Air Abrasion Preconditioning on Microleakage in Class V Restorations Under Cyclic Loading: An In-vitro Study. Journal of Clinical and Diagnostic Research. 2014 Mayo; 8(5): 29-32.
Fu B, Hanning M. Effects of air abrasion and acid etching on the microleakage of preventive Class I resin restorations: an in vitro study. J Esthet Dent.. 1999; 11(3):143-8.
Arezoo J, Hamideh A, Mostafa S. Management of Post-orthodontic White Spot Lesions and Subsequent Enamel Discoloration with Two Microabrasion Techniques. J Dent (Shiraz). 2015 Mar; 16(1): 56-60.
Treviño E. Microabrasion y Operatoria dental. ADM. 2000; 7((3):102-108.
Crim C. Marginal leakage of visible light-cured glass ionomer restorative materials. J. Prost. Dent. 1993; 69: 561-563.
Jiménez A, Yamamoto A. Valoración de la microfiltración del ionómero de vidrio mejorado (Ketac Molar Easymix®) con o sin el uso de acondicionador. Rev Odont Mex. 2015; 19(3) :170-173.
Kleinman L, Anabalón A, Cortés P, Stanke C. Termociclado en la microfiltración de restauraciones cervicales de resina. Rev. dent. Chile. 1997; 88(3):7-10.
Basurto K, Barragán N. Comparación de la microfiltración del Ketac™Molar e Ionofil Molar® con centrix y espátula TRA. CES Odont. 2016; 29 (2): 5-11.
Garrofé A, Martucci D, Picca M. Adhesión a tejidos dentarios. Rev. Fac. de Odon. UBA. 2014; 29(67):5-13.
Salami D, Alves de Cerqueir M. Effect of prophylactic treatments on the superficial roughness of dental tissues and of two esthetic restorative materials. Pesqui. Odontol. 2003 Mar; 17(1): 63-8.
Downloads
Published
Issue
Section
License
- Los autores/as conservarán sus derechos de autor y garantizarán a la revista el derecho de primera publicación de su obra, el cuál estará simultáneamente sujeto a la Licencia de reconocimiento de Creative Commons que permite a terceros compartir la obra siempre que se indique su autor y su primera publicación esta revista.
- Los autores/as podrán adoptar otros acuerdos de licencia no exclusiva de distribución de la versión de la obra publicada (p. ej.: depositarla en un archivo telemático institucional o publicarla en un volumen monográfico) siempre que se indique la publicación inicial en esta revista.
- Se permite y recomienda a los autores/as difundir su obra a través de Internet (p. ej.: en archivos telemáticos institucionales o en su página web) posterior al proceso de aprobación del manuscrito, lo cual puede producir intercambios interesantes y aumentar las citas de la obra publicada.