Evaluation of surface roughness and color stabilityof a nanohybrid resin subjected to diferent salivary pH
Keywords:
Artificial saliva, pH, Composite resin, ColorimetryAbstract
Objective: To determine the surface roughness and color stability of a nanohybrid resin subjected to different salivary pH at different times. Materials and methods: experimental, comparative, in vitro study, in which 45 discs of EA2 nanohybrid resin (OPALLIS FGM), and randomly distributed in three groups (n = 15). Each discs was subjected to an evaluation of its roughness by means of a digital roughness meter (TESTER SRT-6200) and color by colorimeter (Tooth Color Comparator). The discs according to their the group was immersed in 18ml of artificial saliva modified with citric acid until obtaining saliva of pH 5, 6 and 7 respectively, maintained at 37 ° C, according to the specifications of the ANSI / ADA No. 66 standard. After 168 and 504 hours of storage, a second and third evaluation, respectively, of roughness and color, was carried out. Statistical system using the Friedman and Kruskal Wallis test Results: The three salivary pHs modified the surface roughness of the material used in a more evident way, pH 5, observing an increase in surface roughness with the time of exposure to substances with different pH analyzed (p <0.01), the color showed an evident increase of 4 tones in all the samples, with an evident difficulty to analyze statistically. Conclusions: The increase in roughness was proportional with time and inversely proportional with the pH, more evident with pH5, the color evaluation mechanism did not allow obtaining a conclusive data.
Downloads
References
Suarez R, Lozano F. Comparación de la dureza superficial de resinas de nanotecnología, según el momento del pulido: in vitro. Rev Estomatol Herediana [Internet]. 2014; 24(1):11-16.
Chan KH, Mai Y, Kim H, Tong KC, Ng D, Hsiao JC. Review: Resin Composite Filling. PMC. [Internet]. 2010; 3(2):1228–1243.
Demirci M, Tuncer S, Sancakli H, Tekçe N, Baydemir C. Five-year Clinical Evaluation of a Nanofilled and a Nanohybrid Composite in Class IV Cavities. Operative Dentistry [Internet]. 2018; 43(3):261–271.
Tavangar M, Bagheri R., Kwon TY, Mese A, Manton DJ. Influence of beverages and surface roughness on the color change of resin composites. J Investig Clin Dent [Internet}.2018;1(1):1-8.
Satomi T, Pereira T, Vieira F, Ofelia j, Fernando F, Goulart Goyotá F. Restauraciones posteriores con resina compuesta: relato de caso clínico. KIRU [Internet]. 2014; 11(2):175–179.
Arana BE, Achury JL, Coral N, Pulgarin LM, Sepúlveda W. Evaluación del color y rugosidad superficial de resina compuesta después de someterse a enjuagues bucales. Scielo [Internet]. 2014; 5(13): 1-5.
Bhargava A, Sharma D, Majumdar D, Bhargava A, Bansal M, Meel P. Original article “effects of temperature of beverages on ardness, surface roughness and color stabilty of resin composite –an in vitro study. IOSR Journal of Dental and Medical Sciences (IOSR-JDMS) [Internet]. 2016; 8(5):18-23.
İlday N, Bayindir YZ, Erdem V. Effect of three different acidic beverages on surface characteristics of composite resin restorative materials. Materials Research Innovations [Internet]. 2010; 14(5):385–391.
Hwang S, Chung SH, Lee JT, Kim YT, Kim YJ, Oh S, Yeo IS. Influence of Acid, Ethanol, and Anthocyanin Pigment on the Optical and Mechanical Properties of a Nanohybrid Dental Composite Resin. Materials (Basel) [Internet]. [citado Jul 2018];11(7): 1234. 2018; 11(7): p. 1234.
Ulian G, Lia R, Charantola M, Batista E, Kiyoshi S, Wang L. Impact of filler size and distribution on roughness and wear of composite resin after simulated toothbrushing. Scielo [Internet]. [citado Oct 2012];20(5): 1 – 7. 2012; 20(5):1-7.
Coreño-Alonso J, Méndez-Bautista M. Relationship between structure and properties of polymers. Scielo [Internet]. 2010; 4(21):1-11.
Herrera DR, Kose-Jr C, Villa-Verde F, Stanislawczuk R, Reis A, Loguercio AD. Clorhexidina como alternativa para maximizar la longevidad de restauraciones adhesivas. Rev Estomatol Herediana [Internet]. 2010; 20(2):78-84.
Itanto B, Usman M, Margono A. Comparison of surface roughness of nanofilled and nanohybrid composite resins after polishing with a multi-step technique. IOP Publishing [Internet]. 2017; 884:1-7.
Lepri C, Palma R. Surface roughness and color change of a composite: Influence of beverages and brushing. Dental Materials Journal [Internet]. 2012; 31(4):689–696.
Calatrava L. La saliva: una ventana para el diagnóstico. RevVenezInvestOdont IADR [Internet]. 2014; 2(2):65-74.
Aguirre A, Narro SF. Perfil salival y su relación con el índice CEOD en niños de 5 años. Revista Odontológica Mexicana [Internet]. 2016; 20(3):159–165.
Sánchez JC, Urzúa I, Faleiros S, Lira J, Rodríguez G, Cabello R. Capacidad buffer de la saliva en presencia de bebidas energéticas comercializadas en Chile, estudio in vitro. Rev Clin Periodoncia Implantol Rehabil Oral [Internet]. 2015; 8(1):24-30.
Barrios C, Vila V, Martinez S, Encina A. Ph Salival como factor asociado a la caries dental. Revista Facultad De Odontología [Internet]. 2017; 10(1):13-19.
Rodríguez D, Bonilla P, Aillón E, Tello G. Efecto de barnices fluorados sobre el esmalte erosionado a través de microscopia de fuerza atómica: Estudio in vitro. Revista Odontología [Internet]. 2017; 19(1):55–74.
Cengiz S, Yüzbasioglu E, Inanç Cengiz M, Velioglu N, Sevimli G. Color Stability and Surface Roughness of a Laboratory Processed Composite Resin as a Function of Mouthrinse. Journal of Esthetic and Restorative Dentistry [Internet]. 2015; 27(5):314-321.
Moon JD, Son SA, Jung KH, Kwon YH, Park JK. Effect of immersion into solutions at various pH on the color stability of composite resins with different shades. PubMed [Internet]. 2015; 40(4): 270–276.
ANSI/ADA. Procedimientos en Microbiología Clínica. [Online]; 2009. Disponible en: https://www.seimc.org/contenidos/documentoscientificos/procedimientosmicrobiologia/seimc-procedimientomicrobiologia32.pdf. https://sci-hub.se/10.12669/pjms.314.7517 24.
Khan A, Siddiqui A. Effect of different pH solvents on micro-hardness and surface topography of dental nano-composite: An in vitro analysis. Pakistan Journal of Medical Sciences [Internet] 2015;31(4):854-859. Disponible en: https://sci-hub.se/10.12669/pjms.314.7517 24.
Dasilva M, Vitti R, Sinhoreti M, Consani R, Dasilva-Júnior And Tonholo J. Effect of alcoholic beverages on surface roughness and microhardness of dental composites. Dental Materials Journal [Internet]. 2016; 35(4):621–626.
Lamas C, Alvarado S, Angulo G. Importancia del acabado y pulido en restauraciones directas de resina compuesta en piezas dentarias anteriores. Reporte de Caso. Scielo [Internet]. 2015; 25(2):145-151.
Bashetty K, Joshi S. The effect of one-step and multi-step polishing systems on surface texture of two different resin composites. PubMed [Internet]. 2010; 9(6): 1-7.
Lavín S, Toro UG. Cuantificación de la Generación Térmica en Resina Compuesta Sometida a Tres Sistemas de Pulido in vitro. Int. J Odontosmat. [Internet]. 2012[Citado 2020 Oct 21] ;6(3):267-273. Disponible en: http://www.scielo.cl/scielo.php?script=sci_arttext&pid=S0718-381X2012000300004&lng=es.
Downloads
Published
Issue
Section
License
- Los autores/as conservarán sus derechos de autor y garantizarán a la revista el derecho de primera publicación de su obra, el cuál estará simultáneamente sujeto a la Licencia de reconocimiento de Creative Commons que permite a terceros compartir la obra siempre que se indique su autor y su primera publicación esta revista.
- Los autores/as podrán adoptar otros acuerdos de licencia no exclusiva de distribución de la versión de la obra publicada (p. ej.: depositarla en un archivo telemático institucional o publicarla en un volumen monográfico) siempre que se indique la publicación inicial en esta revista.
- Se permite y recomienda a los autores/as difundir su obra a través de Internet (p. ej.: en archivos telemáticos institucionales o en su página web) posterior al proceso de aprobación del manuscrito, lo cual puede producir intercambios interesantes y aumentar las citas de la obra publicada.